| --韩国现代 LL UF414-- |
| |
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
--- |
ASTM D-1238 |
2.0 |
g/10min |
| 密度 |
--- |
ASTM D-1505 |
0.920 |
g/cm3 |
物理性能 |
薄膜厚度 |
--- |
HPC |
40 |
μm |
| 雾度 |
--- |
ASTM D-1003 |
14 |
% |
机械性能 |
落球冲击强度 |
--- |
ASTM D-1709A |
120 |
g |
| 断裂点 |
MD |
ASTM D-882 |
400 |
kg/cm2 |
| 拉伸强度 |
TD |
ASTM D-882 |
370 |
kg/cm2 |
| 断裂伸长率 |
MD |
--- |
ASTM D-882 |
780 |
% |
| TD |
ASTM D-882 |
900 |
% |
| EL撕裂强度 |
MD |
--- |
ASTM D-1922 |
5.0 |
g/μm |
| TD |
ASTM D-1922 |
9.0 |
g/μm |
| 热性能 |
维卡软化点 |
--- |
ASTM D-1525 |
102 |
℃ |
|
（以上数据未经本市场核实） |
|